POLYISOPRENE

Natural rubber is a stereoregular polymer composed of isoprene units attached in a cis configuration. This arrangement gives the rubber high resilience and strength. Isoprene can be polymerized using free radical initiators, but a random polymer is obtained. As with butadiene, polymerization of isoprene can produce a mixture of isomers. However, because the isoprene molecule is asymmetrical, the addition can occur in 1,2-, 1,4- and 3,4- positions. Six tactic forms are possible from both 1,2- and 3,4- addition and two geometrical isomers from 1,4- addition (cis and trans):

Stereoregular polyisoprene is obtained when Zieglar-Natta catalysts or anionic initiators are used. The most important coordination catalyst is α- TiCl₃ cocatalyzed with aluminum alkyls. The polymerization rate and cis content depends upon Al/Ti ratio, which should be greater than one.

Lower ratios predominantly produce the trans structure. Figure 1.1 shows a process for producing cis-polyisoprene by a solution polymerization.

Figure 1.1. A process for producing 1,4-polyisoprene (>99%) by a continuous solution polymerization.

مواضيع ذات صلة

تقدير الكتل المولارية من إتزان الترسب

الأسموزية والديلزة Osmosis and dialysis

الحجم والشكل

الوزن الجزيئي للبوليمرات

البوليمرات المؤلفة من سلاسل رئيسة لا عضوية

البوليمرات ذات مجموعة الروابط الإقترانية

تصنيف مركبات الجزيئات الضخمة ذات السلاسل اللامتجانسة

تصنيف مركبات الجزيئات الضخمة الحاوية على سلاسل كربونية

تصنيف وتسمية مركبات الجزيئات الضخمة

الشكل الهندسي للبوليمر

البوليمرات المشتركة

البوليمرات المنتظمة فراغياً