Linear Low-Density Polyethylene

Linear low-density polyethylene (LLDPE) is produced in the gas phase under low pressure. Catalysts used are either Ziegler type or new generation metallocenes. The Union Carbide process used to produce

HDPE could be used to produce the two polymer grades. Terminal olefins (C4–C6) are the usual comonomers to effect branching.

Developments in the gas-fluidized-bed polymerization reduced investments for high pressure processes used for LDPE. The new technology lowers capital and operating costs and reduces reactor purge/waste streams. Specific designed nozzles are located within the fluidized bed to disperse the hydrocarbons within the bed. The liquid injected through the nozzles quickly evaporates, hence removing the heat of polymerization.

These processes can produce a wide range of polymers with different melt flow indices (MFI of <0.01 to >100) and densities of 890–970 Kg/m3. Types of reactors and catalysts used for HDPE and LLDPE have been reviewed by Chinh and Power.9 LLDPE has properties between HDPE and LDPE. It has fewer branches, higher density, and higher crystallinity than LDPE.

مواضيع ذات صلة

تقدير الكتل المولارية من إتزان الترسب

الأسموزية والديلزة Osmosis and dialysis

الحجم والشكل

الوزن الجزيئي للبوليمرات

البوليمرات المؤلفة من سلاسل رئيسة لا عضوية

البوليمرات ذات مجموعة الروابط الإقترانية

تصنيف مركبات الجزيئات الضخمة ذات السلاسل اللامتجانسة

تصنيف مركبات الجزيئات الضخمة الحاوية على سلاسل كربونية

تصنيف وتسمية مركبات الجزيئات الضخمة

الشكل الهندسي للبوليمر

البوليمرات المشتركة

البوليمرات المنتظمة فراغياً