Beyond the critical diameter of 80 nm, BaTiO₃ stabilises in a cubic structure. Figure.1 shows an increase in the lattice parameter when the average grain size goes down. It would thus seem that there is a grain size dependence in the volume of the unit cell of the crystal lattice. In fact, as we shall see later, this phenomenon is not, at least not for the main part, related to the reduction in size of the nanocrystals, but is due rather to the action of certain heat treatments used on their surfaces to control their size.

In some cases, a grain size dependence is observed in the parameters specifying the crystal structure. However, the few available examples are insufficient to conclude that this is a general effect, and a fortiori, cannot yet provide a full understanding.

Fig.1 Size dependence of the crystallographic lattice parameters a and  c For  BaTiO₃, at 25 ^◦C and standard atmospheric pressure in the powdered state

مواضيع ذات صلة

تشخيص فريت الكوبلت (CoFe2O4) النانوي بواسطة حيود الاشعة السينية

تشخيص فريت الكوبالت (CoFe2O4) النانوي بواسطة طيف الاشعة تحت الحمراء

فريت الكوبلت النانوي CoFe2O4

تحضير فريت الاسبنيل النانوية M=Co, Ni, Cu , Zn) MFe2O) بواسطة الكيمياء الخضراء

العلاج بالضوء Phototherapy

تطبيق المواد النانوية في مستحضرات التجميل Application of nanomaterials in cosmetics

سمية المواد النانوية Toxicity of nanomaterials

تطبيقات المواد النانوية في الأغشية Applications of nanomaterials in membranes

تأثير المواد النانوية على البكتريا الموجودة في الماء Effect of nanomaterials on bacteria in water

اسباب تلوث المياه Causes of water pollution

تطبيق المواد النانوية في معالجة المياه Application of nanomaterials in water treatment

مصير المواد النانوية في التربة Fate of nanomaterials in soil